合金代号 | 密度ρ /g·cm-3 | 熔化温度范围 /℃ | 20～100℃时平均线膨胀系数α /μm·(m·K)-1 | 100℃时比热容с /J·(kg·K)-1 | 25℃时热导率λ /W·(m·K)-1 | 20℃时电导率κ (%IACS) | 20℃时电阻率ρ /nΩ·m |
ZL101 | 2.66 | 577～620 | 23.0 | 879 | 151 | 36 | 45.7 |
ZL101A | 2.68 | 557～613 | 21.4 | 963 | 150 | 36 | 44.2 |
ZL102 | 2.65 | 577～600 | 21.1 | 837 | 155 | 40 | 54.8 |
ZL104 | 2.65 | 569～601 | 21.7 | 753 | 147 | 37 | 46.8 |
ZL105 | 2.68 | 570～627 | 23.0 | 837 | 159 | 36 | 46.2 |
ZL106 | 2.73 | — | 21.4 | 963 | 100.5 | — | — |
ZL108 | 2.68 | — | — | — | 117.2 | — | — |
ZL109 | 2.68 | — | 19 | 963 | 117.2 | 29 | 59.4 |
ZL111 | 2.69 | — | 18.9 | — | — | — | — |
ZL201 | 2.78 | 547.5～650 | 19.5 | 837 | 113 | — | 59.5 |
ZL201A | 2.83 | 547.5～650 | 22.6 | 833 | 105 | — | 52.2 |
Zl202 | 2.91 | — | 22.0 | 963 | 134 | 34 | 52.2 |
ZL203 | 2.80 | — | 23.0 | 837 | 154 | 35 | 43.3 |
ZL204A | 2.81 | 544～650 | 22.03 | — | — | — | — |
ZL205A | 2.82 | 544～633 | 21.9 | 888 | 113 | — | — |
Zl206 | 2.90 | 542～631 | 20.6 | — | 155 | — | 64.5 |
ZL207 | 2.83 | 603～637 | 23.6 | — | 96.3 | — | 53 |
Zl208 | 2.77 | 545～642 | 22.5 | — | 155 | — | 46.5 |
ZL301 | 2.55 | — | 24.5 | 1047 | 92.1 | 21 | 91.2 |
ZL303 | 2.60 | 550～650 | 20.0 | 962 | 125 | 29 | 64.3 |
ZL401 | 2.95 | 545～575 | 24.0 | 879 | — | — | — |
ZL402 | 2.81 | — | 24.7 | 963 | 138.2 | 35 | — |