| 厂家(产地)：韩国锦湖 | 牌号：750NSW | 类型：标准料 |
| 密度：1.04 | 熔体流动速率：5.5 | 成型收缩率：0.55 |
| 规格级别：通用 | 缺口冲击强度：22 | 吸水率：0.3 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 200℃,5kg | ASTM D-1238(ISO 1133) | 5.5 | g/10min |
| 熔体流动速率 | 200℃,10kg | ASTM D-1238(ISO 1133) | 35 | g/10min |
| 吸水率 | ASTM D-5700.3% | |||
| 模塑收缩率 | ASTM D-750.4-0.7% | |||
| 比重 | ASTM D-7921.04 | |||
| 拉伸强度 | 23℃ | ASTM D-638 | 480 | Kg/cm2 |
| 断裂伸长率 | ASTM D-63815% | |||
| 弯曲强度 | 23℃ | ASTM D-790 | 670 | Kg/cm2 |
| 弯曲模量 | 23℃ | ASTM D-790 | 24000 | Kg/cm2 |
| IZOD缺口冲击强度 | 6.4mm | ASTM D-256 | 22 | kg.cm/cm |
| 洛氏硬度 | ASTM D-785110R scale | |||
| 热变形温度 | 6.4mm,18.6kg/cm2未退火 | ASTM D-648 | 85 | ℃ |
| 阻燃性 | UL-94HBclass |